Fabricating PC/PAN composite membranes by vapor-induced phase separation

In this study, a series of polycarbonate/polyacrylonitrile (PC/PAN) composite membrane has been successfully fabricated by vapor-induced phase separation and in-situ casting process. The effect of the casting solution concentration on the membrane morphology was investigated. The morphology of the PC/PAN composite membranes was characterized by SEM. The effect of the skin layer thickness on the water flux was measured at a fixed pressure. Compared with the traditional asymmetric PAN membrane with a dense skin layer and porous support layer, the PC/PAN composite membranes prepared by in-situ casting process effectively prevent the skin layer formation, resulting in the water flux increases.

In this study, a skin-free asymmetric PC/PAN composite membrane was successfully prepared [1] S.J. Shin, J.P. Kim, H.J. Kim, J.H. Jeon and B.R. Min, Preparation and characterization of polyethersulfone microfiltration membranes by a 2-methoxyethanol additive, Desalination, 186 (2005) 1–10. [2] M.H.V. Mulder, Basic Principles of Membrane Technology, Kluwer Academic Publishers, The Netherlands, 1996. [3] H. Caquineau, P. Menut, A. Deratani and C. Dupuy, Influence of the relative humidity on film formation by vapor induced phase separation, Polym. Eng. Sci., 43 (2003) 789–808. [4] H. Matsuyama, M. Teramoto, R. Nakatani and T. Maki, Membrane formation via phase separation induced by penetration of nonsolvent from vapor phase. II. Membrane morphology, J. Appl. Polym. Sci., 74 (1999) 171–178. [5] H.C. Park, Y.P. Kim, H.Y. Kim and Y.S. Kang, Membrane formation by water vapor induced phase inversion, J. Membr. Sci., 156 (1999) 169–178. [6] A.J. Reuvers, Membrane formation. Diffusion induced demixing processes in ternary systems, Ph.D. Thesis, University of Twente, The Netherlands, 1987. [7] C.C. Pereira, R. Noberega and C. P. Borges, Membranes obtained by simultaneous casting of two polymer solutions, J. Membr. Sci., 192 (2001) 11–26. [8] C.C. Pereira, R. Nobrega, K.V. Peinemann and C.P. Borges, Hollow fiber membranes obtained by simultaneous spinning of two polymer solutions: a morphological study, J. Membr. Sci., 226 (2003) 35–50.