... thus facilitating specific water reuse. Membranes can be applied in primary, secondary and tertiary treatment. In this study microfiltration with ceramic membranes (0.1–1.7 µm pore size) was tried out for the activated sludge of a chemi-thermomechanical pulp (CTMP) mill. In the two differen ...
Desalination 146 (2002)

This work investigates the hydrogenation of methylenecyclohexane using catalytic membrane reactors. Flat polymeric (PVDF) and tubular ceramic (γ-Al2O3) membranes were prepared and the hydrogenation catalyst, palladium, was deposited into their porous structure. Characterisations wer ...
Desalination 144 (2002)

... of crossflow microfiltration experiments were used: inorganic * Al2(SO4)3 and organic * PRAESTOL. The experiments were carried out on a tubular ceramic microfiltration membrane with nominal size of pores 0.1 mm at various operating parameters. Preliminary tests were performed before crossflo ...
Desalination 240 (2009)

In the ultrafiltration (UF) of disperse dye solutions using ceramic membrane, backflushing is necessary to minimize the formation of fouling by disperse dye, and to enhance the permeate flux. In this work, th ...
Desalination 202 (2007)

... membranes ranged from 6.5 to 8.0 µm. Polystyrene particles with sizes higher than 7 µm were almost completely removed by the synthesized ceramic membranes; however, no removal for humic acids was measured with the ceramic membranes tested. A new method, AFD, was developed to fabricat ...
Desalination 238 (2009)

... attracting increasingly greater interest because lignin can be extracted from pulping liquors at almost all positions in a pulp mill using ceramic membranes, without altering the pH or temperature of the liquor. In this work hardwood lignin was recovered from two process streams in a kraf ...
Desalination 237 (2009)

... show specific adsorption of Ca2+ and SO42- ions onto the surface. Desalination 235 (2009) 102–109 Electrokinetic characterization of the Al2O3 ceramic MF membrane by streaming potential measurements Jianer Zhoua, Xiaozhen Zhanga*, Yongqing Wanga, Xuebing Hua, A. Larbotb, M. Persinb a Universit ...
Desalination 235 (2009)

... more control of the drop size and size distribution. A drop size of 300– 320 nm with a narrow size distribution was achieved using tubular Al2O3 ceramic membranes (pore size of 200 nm). Based upon the presented results of ectoin permeability into porcine ear skin, it was observed that th ...
Desalination 224 (2008)

... cost. Iron is often added as effective catalyst in the abovementioned AOP. In this study, a 5 kDa molecular weight cut-off (MWCO) ultrafiltration ceramic membrane (TAMI Industries, France) is tested to directly retain iron species from water. The influence of transmembrane pressure, solution pH ...
Desalination 221 (2008)

The ceramic microfiltration system with periodic N2-back-flushing was operated for treating paper wastewater discharged from a company making toilet papers by... was operated for treating paper wastewater discharged from a company making toilet papers by recycling milk or juice cartons. Two kinds of alumina membranes with 7 channels used here for recycling paper wastewater. The optimal N2 filtration time for HC04 membrane with 0.4µm pore size was lower valu ...
Desalination 202 (2006)
 